Passivation could be a non-electrolytic method to removes free iron from the surface associated forms an inert, protecting oxide layer that successively renders the stainless-steel a lot of rust-resistance because of lack of iron to react with the atmosphere by using nitric or citric acid. Here we discuss What is Passivation? How Does Passivation Process Work? How to Passivate Stainless Steel Parts?
Stainless steel is stainless as a result of the protecting Cr oxides on the surface.If those oxides are removed by polishing, or by reaction with bleach, then the iron in the steel is exposed and can be trusted. Passivating stainless steel is typically accomplished in industry by dipping the part in a bath of nitric acid or citric acid.
Nitric acid dissolves any free iron or alternative contaminants from the surface, which cleans the metal, and it re-oxidizes the chromium; all in about 20 minutes. When the surface iron is removed and therefore the alternative elements of the alloy (primarily Cr, often nickel as well) are left behind as a surface layer over the underlying steel. Upon exposure to air, these elements react with oxygen to form an oxide layer that protects the rest of the steel from corrosion.
This corrosion-resistant surface will be broken through mechanical means that or heat or chemical injury. Nitric acid is generally used to passivate stainless steel, but recently a safer and more effective means using citric acid has been introduced. Unlike nitric acid, citric acid also passivates stainless steel.
Nitric acid is generally used to passivate stainless steel, but recently a safer and more effective means using citric acid has been introduced. Unlike nitric acid, citric acid also passivates stainless steel.
Why Citric acid is safer and better than nitric acid for Passivation?
• Citric acid does not remove other elements in the alloy effectively limiting the depth of the final chrome oxide layer. • Citric acid does not introduce heavy metals (hazardous waste) into the bath. • Citric acid only removes iron. • Citric acid is much safer and environmentally friendly because it does not emit harmful nitrogen oxide vapors. • It does not require special handling equipment. • It can also clean and brighten the metal
Passivation disbursed in 2 stages. Stage-1: Removal of free iron or iron compound from the inner surface, free iron or iron compound will produce localized site wherever corrosion will continue, Acid will dissolve away the iron or iron compound. Stage-2: Use of oxidiser to force conversion of Cr to its oxidized to make a layer on the inner surface of the metal to shield the surface from oxidation. 1. Prepare 5%-10% v/v nitric acid solution in water in clean tank or instrumentality. Volume of solution shall be such tank or instrumentality shall not be empty throughout circulation solution through pipe assembly. 2. Connect the each end or one end of involved piece of pipe with acid compatible clean pipe/pipes. 3. One end of the pipe assemble shall be connected to the outlet of the pump and alternative end shall be dippedinto the tank or instrumentality during which solution of nitric acid is ready. 4. start the pump and flow into the solution through the pipe assembly for not but 60 minutes. Once the passivation method is completed, rinse the elements in water or a solution of sodium bichromate(Na2Cr2O7) to neutralize any remaining acid on the surface of the elements, and so drying them. Rinse water pH ought to be check and pH value of the rinse water sample shall be 5.0 to 7.0.
Since passivation involves the use of acids, it ought to be performed by trained personnel only. Person must take adequate protection like using safety goggle or face protect, acid resistance gloves, safety shoe, protecting gowning and alternative instrumentation to keep up safety throughout the operation.
Steel Passivation Specifications:
Passivation processes are generally controlled by industry standards, the most prevalent among them today being
ASTM A 967-01
Specification for Chemical Passivation Treatments for Stainless Steel Parts (based on US Defense Department standard QQ-P-35C) – one of the most common passivation specifications
Passivation of Corrosion resistant steels
Passivation Treatment for corrosion resistant Steel
ASTM A 380-99
Practice for Cleaning, Descalling and passivating os stainless steel parts, equipment and systems
Standard Practice for surface Preparation and Marking of Metalic Surgical ImplantsAMS 2700